Photocatalytic and Photo-Fenton-like Degradation of Methylene Blue Using Green-Synthesized Phosphate-Doped ZnO Under Visible LED Light

Water pollution caused by synthetic dyes is a major environmental concern due to their stability, toxicity, and resistance to conventional wastewater treatments. This study presents a sustainable approach for synthesizing zinc oxide (ZnO) nanoparticles using artichoke biomass (waste) as a green precursor and enhancing their visible light photocatalytic activity through phosphorus doping. ZnO nanoparticles were successfully synthesized via a simple green route and doped with 3–6% phosphorus using NH4H2PO4. The structural, morphological, and optical properties of the resulting P-ZnO were characterized by XRD, SEM/EDX, TEM, FTIR, and UV-Vis spectroscopy. (6 wt%) Phosphorus doping effectively reduced the band gap from 3.06 eV to 2.95 eV, extended light absorption into the visible range, and improved electron–hole separation, resulting in enhanced photocatalytic performance. The P-ZnO nanoparticles were evaluated for methylene blue (MB) degradation under visible light in a photo-Fenton-like process, with H2O2 as an oxidant. The degradation efficiency reached 87.05% with 6% P-ZnO and further increased to 92.35% upon addition of H2O2. Durability and reusability tests demonstrated that the 6% P-ZnO catalyst maintained its activity and structural integrity over four consecutive cycles, indicating negligible loss of efficiency and excellent resistance to surface poisoning. The photocatalytic activity was strongly impacted by the quantity of catalyst, solution pH, and initial dye levels, with optimal performance at 0.3 g/L catalyst loading, pH 3, and lower MB concentrations.