A Comparative Study of Waste Red-Clay Brick Powder (WRCBP) and Fly Ash (FA) as Precursors for Geopolymer Production

Utilizing waste red-clay brick powder (WRCBP) as a precursor for manufacturing geopolymers is increasingly popular due to its environmental and economic benefits. However, the geopolymerization of this waste remains insufficiently explored. This study evaluates the differences in physical–mechanical properties and microstructural evolution of WRCBP- and fly ash (FA)-based geopolymers to determine the reactivity of WRCBP. Mineral admixtures, including granulated blast furnace slag (GF) and metakaolin (MT), were incorporated with WRCBP to fabricate geopolymer pastes, while FA was used in parallel for comparison. The effects of activator modulus (1.2 and 1.4 for Na2SiO3) and curing conditions (65 °C and 90 °C) on the mechanical and microstructural performance of the prepared pastes were investigated through water demand analysis, compressive strength testing, mercury intrusion porosimetry (MIP), and scanning electron microscopy (SEM). The results indicate that WRCBP-based pastes achieved a comparable compressive strength (39.8 MPa) under appropriate alkali-activated and curing conditions relative to FA-based pastes (42.5 MPa). The modulus of the alkaline activator exerted a greater influence on strength development than the raw material composition. For both WRCBP- and FA-based pastes, 65 °C was identified as a more suitable curing temperature. Moreover, compared with FA-based pastes, pastes produced using WRCBP provide enhanced social and economic benefits. Overall, this study confirms that high-performance binders can be engineered by incorporating WRCBP, thereby supporting the development of sustainable low-carbon construction materials.