High-Temperature Neutron Diffraction Study of Vanadium and Vanadium–Niobium Null-Matrix Alloy for Spectrum Normalization

This study systematically evaluates a vanadium–niobium (V94.1Nb5.9) null-matrix alloy as a reference material for neutron spectrum normalization and compares its performance with that of pure vanadium under identical experimental conditions. Neutron diffraction experiments are conducted on the VULCAN Engineering Materials Diffractometer at the Spallation Neutron Source, Oak Ridge National Laboratory, over a temperature range from room temperature to 1200 °C under vacuum. Pure vanadium exhibited distinct Bragg peaks across all temperatures, with its diffraction behavior influenced by both sample orientation and temperature. As the temperature increased, the diffraction peaks shifted to larger d-spacings and decreased in intensity, while spectral deviation near d ≈ 2.8 Å exceeded 10% at 1200 °C. In contrast, the V–Nb alloy produced a nearly featureless spectrum over the full d-spacing range, confirming near-complete cancellation of coherent scattering over the wide temperature range. Its spectra were insensitive to sample orientation, temperature, and microstructural evolution, with spectral deviation around d ≈ 2.8 Å exceeded 5% at 1200 °C. These results demonstrate that the V–Nb null-matrix alloy provides a thermally stable, efficient, and reliable normalization standard for time-of-flight diffractometers or other instrument where it is needed, enabling reduced data acquisition time and improved data quality in high-temperature neutron diffraction experiments.