The interaction of edge dislocations with hydrogen-helium bubbles in tungsten

In fusion reactors, plasmas-facing components undergo degradation due to displacement damage and injection of gas impurities. Significant amounts of hydrogen (H) and helium (He) impurities can be introduced into materials through plasma exposure and nuclear transmutation, and their synergistic effects lead to the formation of mixed He/H bubbles under irradiation, changing their hardening mechanisms. In this study, molecular dynamics (MD) models were developed to study the interaction between ½<111> edge dislocations with mixed He/H-bubbles in W. The critical resolved shear stress (CRSS) that is required for dislocation breakaway increases with He/H-to-vacancy ratio at 600 K, indicating strong pinning effects of mixed He/H bubbles. However, as the temperature increases up to 1400 K, the mixed He/H bubbles become unstable as the H atoms are increasingly emitted from the mixed He/H bubbles and migrate into W matrix, which lowers bubble pressure and CRSS. Overall, these results highlight the synergistic effects of He and H on dislocation behavior in irradiated W during deformation.