The Influence of Y2O3 Dosage on the Performance of Fe60/WC Laser Cladding Coating

To prepare a high-performance Fe-based laser cladding coating, herein, various Fe60/WC/Y₂O₃ coatings are deposited on the surface of 42CrMo steel plate via a laser cladding technique. The WC dosage is fixed as 10 wt%, while the dosage of Y₂O₃ ranges from 0 to 7.5 wt%. The influences of Y₂O₃ dosage on the coating hardness, wear resistance, and corrosion resistance are investigated. With the addition of Y₂O₃, the feature peak of WC disappears, and the peaks of M₂₃C₆ gradually weaken, indicating that Y₂O₃ promotes the decomposition of WC and suppresses the formation of new metal carbides. When the dosage of Y₂O₃ is 2.5 wt%, a grid-like structure is formed on the coating surface, suggesting uniform distribution of decomposed W within the Fe matrix. When the Y₂O₃ dosage exceeds 5 wt%, a large amount of CO₂ gas is released, leading to an increase in surface pores. Through a comparison, the optimal dosage of Y₂O₃ is 2.5 wt%, and the resulting 3# coating has the highest hardness of 861.97 HV. Moreover, the 3# coating also shows the minimum friction coefficient and the minimum wear volume, reflecting its superior wear resistance. The polished coating serves as a working electrode, and the corrosion resistance is tested in 3.5% NaCl solution. The sample containing 2.5 wt% Y₂O₃ has the highest corrosion potential and the lowest corrosion current density, indicating excellent corrosion resistance. The enhanced performance is ascribed to the improved surface quality and the formation of a W-reinforced grid structure. The high-performance coating has promising application potential in material and component repair.