Proton Binding of Halloysite Nanotubes at Varied Ionic Strength: A Potentiometric Titration and Electrophoretic Mobility Study

Proton binding (i.e., charging) isotherms of halloysite nanotubes (HNT) were determined from cycled acid-base potentiometric titrations in KCl solution at constant ionic strengths (0.01, 0.10, 1.00 mol dm−3). The isotherms measured in the pH cycle from 3 to 11 and back exhibit a pronounced hysteresis with respect to the direction of pH change, which is accurately reproducible when the cycle is repeated. The hysteresis is absent if the cycled titration is performed within a narrow pH range between 5 and 9. These results align with the dissolution rates of alumina and silica, which form the two surfaces of the rolled kaolinite sheet in HNT, and clearly point to reversible partial dissolution-deposition processes in the HNT interior during a titration cycle, outside the above pH range (alumina dissolution below pH ≈ 5 and silica dissolution above pH ≈ 8.5). In the studied titration experiments, these processes produce partially dissolved surface-bound, rather than completely dissolved species (reversible surface etching). Under the applied conditions, reversible surface etching is less pronounced in the acidic part of the titration cycle. Charging isotherms recorded in the decreasing pH titrations at varied ionic strength exhibit a common intersection point very close to zero charge (point of zero charge) around pH ≈ 8.1, characteristic for an amphoteric solid surface. These isotherms were reasonably well fitted by applying the surface protonation model in the HNT interior, which invokes the Stern model of the electric double layer (EDL), by summing the surface charges calculated for alumina and silica as separate components (surfaces). The model surface charge isotherms for alumina surface in the HNT interior exhibit a point of zero charge at pH = 9.0, while the silica surface has a negative charge above pH > 8.5, which is in very good agreement with the values reported in the literature: as for these two surfaces, thus for kaolinite nanoparticles. The best-fit protonation site density for both surfaces is equal to 8.0 nm−2, while the best-fit intrinsic pKa for alumina and silica surfaces of HNT are equal to 9.0 and 8.5, respectively. The pH-dependence of electrophoretic mobility, measured by means of electrophoretic light scattering, reveals a more acidic behavior of the outermost silica surface than within the inner HNT phase, which is consistent with the literature result reported for kaolinite. The results reported herein confirm that the inner and outer surfaces of the HNT are oppositely charged below pH < 8.0 and negatively charged above that value, and importantly, they reveal new details about the protonation affinities and EDL parameters at active surfaces of HNT, important for the colloidal stability of HNT suspensions and the functionalization of HNT through the electrostatic binding of active molecules.