The Impact of Phase Change in Laser-Ablated Aluminum Alloy Materials on Ablation Damage Characteristics

Laser weapons, characterized by their rapid response capabilities, precision targeting, and operational stealth, have emerged as essential directed energy systems for neutralizing missile, satellite, and drone threats. This paper examines the widely utilized 7075 high-strength aluminum alloy in military applications, conducting a comprehensive analysis of the material’s ablation characteristics under continuous laser exposure. The study elucidates the phase change phenomena and elemental separation mechanisms that occur as a result of ablation. Findings indicate that the aluminum (Al) element primarily undergoes a process of melting, driven by gravitational flow and subsequent resolidification, resulting in the formation of a bright silver Al-rich solidified layer at the base of the ablation zone. Conversely, the zinc (Zn) element vaporizes at elevated temperatures, with its byproducts oxidizing and condensing in the atmosphere, leading to the formation of gray- white zinc oxide (ZnO) deposits above the ablation area. This research highlights the synergistic damage mechanisms of vaporization and melting, thereby providing a critical theoretical framework for understanding the damage mechanisms associated with laser ablation of aluminum alloys.