Corrosion analysis of Al-Ce-Ni and Al-Cu-Ce cast alloys in dilute boric acid at room and elevated temperatures

Two Al-Ce-Ni cast alloys, and an Al-Cu-Ce cast alloy, as candidate wet storage materials for spent nuclear fuels, were tested in 0.23 wt.% H 3 BO 3 solution to assess the alloy corrosion resistance. Electrochemical and gravimetric corrosion data suggest that the three Al alloys are unlikely to undergo any severe corrosion in dilute H 3 BO 3 at or below 50 °C. Post-exposure characterization of the three Al alloys, including scanning and transmission electron microscopy and electron dispersive spectroscopy, revealed a corrosion product layer, mostly Al 2 O 3 , on the exposed surface and local penetration of oxygen into the alloy matrix. The degree of oxide layer growth and oxygen penetration is greater at 80 °C than the temperature at/below 50 °C. The Al-Cu-Ce alloy is considered less corrosion resistant than the other two alloys studied.