Mechanochemical Optimization of Composite–Substrate Interfaces for Durable Repair Adhesion to Metal and Zirconia: An In Vitro Study

Background/Objectives: Achieving durable intraoral repairs of fractured metal and zirconia restorations requires optimal adhesion. This in vitro study evaluated the effects of mechanical surface treatments and commercial repair systems on the shear bond strength (SBS) of composite resin to nickel–chromium (Ni-Cr) alloy and zirconia, including the influence of thermocycling aging. Methods: In this study, 144 Ni-Cr and zirconia discs (12 × 12 × 2 mm) were randomly assigned to three surface treatments: untreated control, airborne particle abrasion (50 µm Al2O3), and medium grit diamond bur grinding. Each group was further subdivided to assess two intraoral repair kits (GC Corp (Tokyo, Japan). and Bisco Inc. (Schaumburg, IL, USA)). Composite resin cylinders were bonded following the manufacturer’s instructions. Half of the specimens (n = 12/subgroup) underwent 5000 thermocycles (5–55 °C). Micro-shear bond strength testing was performed, and failure modes were analyzed. Data were analyzed using three-way ANOVA and post hoc tests (p < 0.05). Results: Air abrasion significantly increased SBS compared to control and bur grinding for metal (p < 0.001). For zirconia, both air abrasion and bur grinding yielded similarly improved SBS over the control (p < 0.001). The GC repair kit demonstrated significantly superior bond stability after thermocycling across both substrates. Aging significantly reduced SBS in all groups (p < 0.001), with the most substantial reductions observed in untreated controls and groups repaired with the Bisco system. Conclusions: Airborne particle abrasion combined with a HEMA-free, 10-MDP-containing universal adhesive achieved the strongest and most durable resin bonds to both metal and zirconia, supporting its clinical use for the intraoral repair of ceramic and metal restorations.