Study on the Interfacial Bonding Behavior of OPC-GGBS-SAC Composite Repair Materials

The bonding interface between repair materials and concrete substrate is the weakest link in the entire repair structure. If the interface bonding performance is insufficient, the repair material is prone to cracking or falling off, leading to repair failure. The shrinkage of repair materials is one of the primary factors affecting the bonding performance of these interfaces. In this study, sulphoaluminate cement (SAC) was used to improve the repair performance of ordinary Portland cement (OPC)–granulated blast furnace slag (GGBS) composite repair materials. The influence of SAC on the mechanical properties, bonding performance, expansion behavior, impermeability, and hydration heat of OPC-GGBS-SAC composite repair materials was investigated. The results demonstrate that the rapid hydration of SAC significantly improved the early strength and mechanical properties of the composite system at negative temperatures. The hydration products filled the pores within the concrete matrix, thereby enhancing the mechanical meshing effect at the interface. The early expansion effect of SAC formed a pre-stressor at the interface, which not only strengthened the bonding force between repair materials and the substrate, but also effectively inhibited the shrinkage of the composite system and prevented crack formation, thus significantly promoting the long-term reliability of the bonding interface. An appropriate amount of SAC can accelerate the hydration process of OPC-GGBS system, advance the exothermic peak, and promote the development of early strength. However, excessive incorporation will inhibit the later hydration of the composite system due to the way in which the hydration products wrap the cement particles. When the content of SAC was 5–10%, optimal comprehensive properties of the OPC-GGBS-SAC composite system were attained.