Minimization of Cathode|Solid-Electrolyte Interfacial Delamination through the Application of Interphase Layers

Next-generation lithium-ion batteries are expected to use solid electrolytes (SEs) to enable higher energy density and extreme fast-charge capabilities. One major mode of degradation at the cathode|SE interface is delamination between the cathode active materials and SEs, which leads to performance decay. Experimental observations indicate that implementation of interphase layers can minimize the cathode|SE delamination induced capacity fade. A multiscale computational methodology is developed here to investigate the applicability of boron substituted lithium carbonate (Li2+xBxC1–xO3, x = 0.5, or LBCO) to minimize the delamination at the cathode|SE interface. Atomistic simulations indicate that the fracture energies at both the cathode|LBCO and LBCO|SE interfaces are higher than those at the cathode|SE interface, which reduces the extent of delamination. Mesoscale simulations indicate that, apart from increasing the fracture energy, decreasing the evolution of strain energy by lowering the elastic modulus of the interphase layer can also minimize the extent of delamination at the cathode|SE interface. However, the adoption of an interphase layer with high ionic conductivity is necessary to minimize the ohmic losses during operation at higher current densities. This study provides guidance on selecting interphase layers with specific properties and thicknesses to minimize both interfacial delamination and impedance growth.