Performance and Environmental Assessment of Alkali-Activated Cements from Agricultural and Industrial Residues

The growing concern with carbon dioxide emissions from the cement industry has driven the search for alternative binders with lower environmental impact. Among these, alkali-activated cements (AACs) stand out due to their ability to produce cementitious matrices from aluminosilicate precursors and alkaline activators. However, comparisons between One-Part and Two-Part systems remain limited. This study evaluated the technical feasibility of producing AAC using sugarcane bagasse ash (SCBA) as precursor, carbide lime (CL) as calcium source, and sodium hydroxide (NaOH) as activator. Different parameters were tested, including NaOH molarities (1.0–2.5 M), SCBA/CL ratios (9.00–1.50), curing times (3, 7, and 28 days), and preparation methods. Mortars were produced at constant water/solid ratio of 1.40 and cured at room temperature (23 °C). Unconfined compressive strength (UCS) and leaching tests were performed, along with statistical analysis and Scanning Electron Microscopy (SEM), X-ray Diffraction (XRD), and Fourier Transform Infrared Spectroscopy (FTIR) analyses. ACC synthesized by the Two-Part method (2.0 M NaOH, SCBA:CL 70:30) reached an UCS of 1.60 MPa at 28 days, compared to 1.39 MPa for the One-Part method. Curing time was identified as the most significant factor, followed by SCBA/CL ratio and activator molarity, while preparation method had minimal effect. The material developed alkali-activated gels, and leaching tests indicated no toxicity, although Ba concentrations exceeded regulatory limits for water quality. Potential applications include mine tailings stabilization, soil improvement, shallow foundations, and urban furniture production.