Impact Butt Joining of Copper C1100 and Aluminum Alloy A6061-T6 Plates and Rolling of Joined Plate

Impact butt joining of copper 5 mm thick C1100 and aluminum alloy A6061-T6 plates was carried out, according to a method recently devised by one of the authors. The joining method results in newly created surfaces being obtained by very large plastic deformation under high-speed conditions, wherein the two materials are subjected simultaneously to compression and a high-speed sliding motion. The new surface of C1100 is created by expansion, whereas for A6061-T6, the new surface is created by removal of the softened surface layer. This layer forms a foil, which is extruded from the joining interface by the compressive force. Using a high-speed video camera, the formation of the foil was observed to take place even in the early stages of deformation. The distribution of joint efficiency was evaluated by examining the joint boundary. When the compressive force increased, some specimens fractured in the C1100 region. The zone affected by the joining process was highly limited, to within 0.8 mm of the boundary; i.e., 20% of the plate thickness. The thickness of the joined plate was reduced by repetitive rolling operations, in which the true strain was about −1. This indicates that the layer of the intermetallic compounds is very thin. Once rolled, the joined sheet exhibited a maximum joint efficiency of 99.3%. In cases where the joining efficiency exceeded 80%, the main region exhibiting fracturing was in the A6061-T6 alloy.