High-Temperature Tensile Properties in the Curved Continuous Casting of M2 High-Speed Steel

The industrial production of high-speed steel via continuous casting has been impeded by considerable technical obstacles, due to its high carbon content and fast cooling speed, which predispose it to severe segregation and poor high-temperature plasticity; thus, industrial continuous casting of high-speed steel is virtually nonexistent. In 2022, a curved continuous casting process was successfully applied in the production of M2 high-speed steel; in our previous study, it was found that the carbides were finer and better distributed in the billets by curved continuous casting than those in the billets by ingot casting. The change in carbides in the billets is significant in subsequent processes for M2 high-speed steel produced by curved continuous casting. Therefore, it is necessary to investigate the high-temperature tensile properties of M2 high-speed steel produced by curved continuous casting. In this paper, high-temperature tensile tests were conducted using a GLEEBLE-3500 simulator (DSI, located in New York State, USA) at different temperatures and holding times with a certain strain rate to obtain the tensile strength and reduction of area, and then the morphology of carbides near the fracture surface was observed. The results showed that the tensile strength and reduction of area increased with the increase in temperature at 850 °C to 950 °C, and there existed a temperature range between 950 °C and 1120 °C with good thermoplasticity and a reduction of area from 45% to 50%. In addition, a sharp drop in thermoplasticity below 5% occurred at 1180 °C, which is due to the significant growth of carbides. The zero-strength temperature and plastic temperature were 1220 °C and 1200 °C, respectively. In addition, with the increase in holding time at 1150 °C, the reduction of area increased from 34% to 54%, and the tensile strength decreased from 92 MPa to 70 MPa and then increased to 82 MPa. The best solution for carbides in M2 high-speed steel produced by curved continuous casting occurred when the range of the PHJ value was about 28.0 to 30.5. With the increase in PHJ value, the shape of carbides gradually changed from fibrous to short rod-like and blocky during high-temperature diffusion.