Shot Blasting for Enhancing Wear Resistance and Impact Resistance of SCMnH11 High-Manganese Steel

In this study, shot blasting was employed to enhance the wear resistance and impact toughness of SCMnH11 high-manganese steel. The steel was first fabricated via vacuum casting, followed by forging and water-toughening treatment. Subsequently, the steel was cut to the required dimensions using wire electrical discharge machining before the final shot blasting was performed. The influence of shot blasting duration on the microstructure and mechanical properties was investigated. Shot blasting introduced compressive residual stress and dislocations, resulting in the formation of numerous low-angle grain boundaries. As the shot blasting time increased, the surface grains were progressively refined. The surface hardness increased rapidly from an initial value of approximately 250 HV, reaching a maximum of 643 HV. After 60 min of shot blasting, the thickness of the surface hardened layer reached 600 µm; however, the surface hardness exhibited a trend of first increasing and then decreasing. In contrast, the wear resistance showed the opposite trend. Additionally, the dominant surface wear mechanism transitioned from adhesive wear in the heat-treated sample to abrasive wear in the shot-blasted samples. Compared to the heat-treated sample, the impact toughness of the samples subjected to 5 min and 60 min shot blasting was significantly enhanced. Correspondingly, the fracture mechanism shifted from predominantly ductile fracture to a mixed mode of ductile and cleavage fracture. In summary, shot blasting can effectively enhance the wear resistance and impact resistance of SCMnH11 steel. However, the selection of shot blasting duration is critical. Appropriate parameters can balance work hardening, compressive stress, and surface microcracks, thereby enabling the material to achieve an optimal combination of wear resistance and impact resistance.