Effect of Nickel Alloying on the Glass-Forming Ability and Corrosion Resistance of a Pt-Pd-Cu-P Bulk Metallic Glass

This study systematically investigates the effect of substituting Copper (Cu) with Nickel (Ni) on the glass-forming ability (GFA) and corrosion resistance of a Pt-based bulk metallic glass (BMG). We demonstrate that a minor substitution of 5 at.% Ni for Cu in the Pt40Pd20Cu20P20 base alloy significantly enhances both properties. The GFA is markedly improved, as evidenced by the supercooled liquid region (ΔTx) widening from 68 K to 91 K. The optimized Pt40Pd20Cu15Ni5P20 alloy exhibits a compressive fracture strength of 1.38 GPa. Electrochemical tests in a 3.5 wt.% NaCl solution reveal a substantial improvement in corrosion resistance. Compared to the Ni-free baseline alloy, the passive film resistance (Rf) and charge-transfer resistance (Rct) of the Ni-containing alloy are enhanced by factors of 2.75 and 2.60, respectively. This superior performance is attributed to a synergistic effect wherein Ni alloying both stabilizes the amorphous structure and promotes the formation of a more robust passive film. This work presents a viable strategy for designing cost-effective, high-performance multi-component BMGs for applications in aggressive chloride environments.