One-Pot Preparation of Easily Dispersible Hexagonal Mg(OH)2 Modified with THPS and Its Flame-Retardant EVA Copolymer

As an eco-friendly flame-retardant additive, magnesium hydroxide (MH) is widely employed in low-smoking, halogen-free polymer materials due to its environmentally benign nature. In order to enhance flame retardancy performance, the modified MH was modified with tetrakis(hydroxymethyl)phosphonium sulfate (THPS) by a one-pot hydrothermal method. The resulting morphology was characterized using scanning electron microscopy (SEM), and it shows the dispersion of nanometer particles and almost no aggregation. The X-ray photoelectron spectroscopy (XPS) along with Raman spectroscopy show that the THPS is connected with the Mg(OH)₂ by chemical bond. The sample was incorporated into ethylene-vinyl acetate (EVA) to evaluate the flame retardancy was assessed via limiting oxygen index (LOI) and vertical burning tests (UL-94). The results show that THPS modified MH effectively enhanced the flame retardancy, achieving a V-0 rating and an LOI value of 31.3%. In addition, the composites retain good mechanical integrity. The thermal analysis with TGA and DTG shows the formation of the MgO decomposition product, along with water vapor and phosphorus-containing radicals released by modified MH in the combustion process, forming a strong flame-retardant protective layer. In addition, the maximum smoke density of EVA/MHP-3 composite was 155.4, lower than 411.3 for EVA/MH, with a 62.2% reduction in total smoke production. The result shows that THPS is effective for improving the flame-retardant efficiency of inorganic metal hydroxide in polymer composites.