Research and Application of Top and Bottom Combined Argon Blowing for 300t Ladle

This article uses a water model with a ratio of 1:5.75 to study the influence of factors such as the position and flow rate of top and bottom composite argon blowing on the mixing time of molten steel in a 300t ladle at a certain factory. Using engine oil to simulate steel slag, the mass transfer velocity of molten steel under different bottom and top blowing positions and flow rates of the ladle was compared. At the same time, numerical simulation was used to analyze the changes in the flow field of molten steel under different ladle blowing modes. The optimal ladle composite bottom argon process was proposed and industrial experiments were conducted on site. The research results show that the stirring effect of top–bottom composite argon blowing in the ladle is significantly better than that of the pure bottom blowing mode. When the top blowing gun is located 300 mm at the bottom of the ladle, the mixing time of the molten steel is shortest and the stirring efficiency is highest. The higher the insertion depth of the top blowing gun, the faster the flow rate of the molten steel, and the smaller the proportion of dead zones. Top and bottom blowing can improve the mass transfer rate between steel slag and promote the formation of refined slag. Through industrial experiments, it was found that the S content in the molten steel decreased by approximately 22.3% and the total oxygen content decreased by 25% before and after 10 min of composite argon blowing at the top and bottom of the ladle.