Role of Salt Concentration on Interphase Dynamics and Chemistry of Silicon Anodes during Electrochemical Cycling

We investigated the chemistry and structure of the solid electrolyte interphase (SEI) grown over a silicon anode as a function of the lithium salt concentration. In these experiments, in situ neutron reflectivity measurements were performed to measure the thickness and composition of the SEI formed from 1.0 and 5.5 M lithium bis(trifluoromethane)sulfonimide (LiTFSI) in standard ethylene carbonate:dimethyl carbonate electrolytes. These measurements reveal the formation of a 350+ Å thick SEI layer that is predominantly organic (∼80%) and dimensionally stable when using a 1.0 M salt solution. In contrast, increasing the salt concentration to 5.5 M resulted in an SEI that exhibited thickness changes from 100 to 375 Å and became up to 30% inorganic. These compositional and structural changes point to the role of salt speciation on the resulting passivation of silicon electrodes and indicate the need to form more organic-like passivation layers to promote the calendar life of silicon anodes.