Tailoring microstructure and strength-ductility synergy in AZ91D/ZrO₂ magnesium matrix composite by dual eccentric-pin tool friction stir processing

• Dual eccentric-pin tool (DEPT) FSP was employed to incorporate ZrO 2 particles AZ91D Mg alloy. • Enhanced twin formation and dislocation distribution. • Transition from basal to prismatic texture. • Strength-ductility synergy significantly improved. The inherent trade-off between ductility and strength in Mg alloys remains a significant challenge, primarily governed by microstructural distribution and texture characteristics. Friction stir processing (FSP), a severe plastic deformation (SPD) technique, refines microstructures by generating fine grains, uniformly dispersed fragmented particles, and a high fraction of high-angle grain boundaries (HAGBs), thereby facilitating superplastic forming at high strain rates and low temperatures. In the present work, a dual eccentric-pin tool (DEPT) FSP was employed to incorporate ZrO₂ particles into a 6 mm thick AZ91D Mg alloy, leading to the formation of high volume {10–12} twins, dislocations, and β-Mg₁₇Al₁₂ precipitates within the stirred zone. The microstructural evolution and mechanical behaviour of the stir zone under various process parameters were analysed using scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM). The DEPT enhanced plastic shearing and dynamic recrystallization, significantly reducing the grain size from 15.6 µm to 2.35 µm while promoting uniform dislocation distribution within the stir zone (SZ). Grain orientation analysis revealed a transition from basal to prismatic texture dominance (29.3% volume fraction) due to intensified radial-tangential coupling shear deformation, facilitating the activation of non-basal slip systems. The DEPT evidently improved the hardness of the SZ from 58 to 92 HV and increased tensile strength from 234 MPa to 325 MPa while maintaining an elongation of 23.8%, achieving an optimal strength-ductility balance. This work presents a one-step approach for tailoring microstructural heterogeneity and enhancing mechanical properties in AZ91D/ZrO₂ composites using the DEPT FSP technique. The method provides an effective strategy for mitigating the strength–ductility trade-off commonly observed in Mg alloys.

Authors

Institutions

Publication Details

Journal
Journal of Magnesium and Alloys
Published
2025-10-22
DOI
https://doi.org/10.1016/j.jma.2025.08.037
Citations
2
Primary Topic
Aluminum Alloys Composites Properties
Type
article
Field-Weighted Citation Impact
1.43
Controls
|||
ALL TIME
JAN
FEB
MAR
APR
MAY
JUN
JUL
AUG
SEP
OCT
article

Tailoring microstructure and strength-ductility synergy in AZ91D/ZrO₂ magnesium matrix composite by dual eccentric-pin tool friction stir processing

Long Li, Chuansong Wu, Surendra Kumar Patel, Xiang Zhang et al.
2 citations
Journal of Magnesium and Alloys
Aluminum Alloys Composites Properties
1.43
article

Tailoring microstructure and strength-ductility synergy in AZ91D/ZrO₂ magnesium matrix composite by dual eccentric-pin tool friction stir processing

Long Li, Chuansong Wu, Surendra Kumar Patel, Xiang Zhang, Lei Shi, Ashish Kumar, Virendra Pratap Singh, Zheng Lu
article en
2 citations

Abstract

• Dual eccentric-pin tool (DEPT) FSP was employed to incorporate ZrO 2 particles AZ91D Mg alloy. • Enhanced twin formation and dislocation distribution. • Transition from basal to prismatic texture. • Strength-ductility synergy significantly improved. The inherent trade-off between ductility and strength in Mg alloys remains a significant challenge, primarily governed by microstructural distribution and texture characteristics. Friction stir processing (FSP), a severe plastic deformation (SPD) technique, refines microstructures by generating fine grains, uniformly dispersed fragmented particles, and a high fraction of high-angle grain boundaries (HAGBs), thereby facilitating superplastic forming at high strain rates and low temperatures. In the present work, a dual eccentric-pin tool (DEPT) FSP was employed to incorporate ZrO₂ particles into a 6 mm thick AZ91D Mg alloy, leading to the formation of high volume {10–12} twins, dislocations, and β-Mg₁₇Al₁₂ precipitates within the stirred zone. The microstructural evolution and mechanical behaviour of the stir zone under various process parameters were analysed using scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM). The DEPT enhanced plastic shearing and dynamic recrystallization, significantly reducing the grain size from 15.6 µm to 2.35 µm while promoting uniform dislocation distribution within the stir zone (SZ). Grain orientation analysis revealed a transition from basal to prismatic texture dominance (29.3% volume fraction) due to intensified radial-tangential coupling shear deformation, facilitating the activation of non-basal slip systems. The DEPT evidently improved the hardness of the SZ from 58 to 92 HV and increased tensile strength from 234 MPa to 325 MPa while maintaining an elongation of 23.8%, achieving an optimal strength-ductility balance. This work presents a one-step approach for tailoring microstructural heterogeneity and enhancing mechanical properties in AZ91D/ZrO₂ composites using the DEPT FSP technique. The method provides an effective strategy for mitigating the strength–ductility trade-off commonly observed in Mg alloys.

Journal of Magnesium and AlloysVol. 13(11)
Shandong University (CN), Qilu Hospital of Shandong University (CN), Delhi Technological University (IN)
Openalex Percentile: Top 17%
Aluminum Alloys Composites Properties
1.43
AI Navigator

Ask Laika to Summarize, Analyze, and Connect papers live on the map.

Summarize Papers & Methodologies

Extract key findings, datasets, and comparative methods across publications.

Benchmark Rankings & Visual Analytics

Rank top research institutions, authors, funders, topics, and journals by Field-Weighted Citation Impact (FWCI) and paper volume with instant charts.

Connect Distant Disciplines

Bridge topological clusters on the map to find hidden collaborative intersections.