Fabrication of Graphite Flake/Al Composites via the Hybrid Powder-Melt Process: Synergistic Enhancement of Strength and Conductivity Through Low Content Addition

This study addresses the challenge of simultaneously improving the electrical conductivity and strength of aluminum alloys. We innovatively combine powder metallurgy with melt stirring casting to fabricate graphite flake-added aluminum matrix composites through secondary remelting, electromagnetic stirring, and extruding. The influence of graphite flake content gradient (0-3.0 wt.%) on the mechanical properties and electrical conductivity was systematically investigated. Our results demonstrate that the composite with 0.2 wt.% graphite flakes (sample GM02) exhibits optimal comprehensive performance: tensile strength reaches 100.9 MPa (a 124% increase over pure Al), and electrical conductivity reaches 67.1% IACS (a 9.6% increase). Microstructural analysis reveals that low-content graphite flakes effectively suppressed electron scattering by forming semi-coherent interfaces. However, when graphite flake content exceeds 0.5 wt.%, a significant decrease in conductivity and plasticity (elongation below 10%) occurs due to increased Al₄C₃ phase formation, enhanced grain boundary scattering caused by grain refinement, and porosity defects induced by graphite flake agglomeration. This study provides a novel approach for the industrial production of high-performance, lightweight conductive components.