The influence of laser power modulation on melt pool dynamics in laser powder bed fusion

While the majority of laser powder bed fusion (LPBF) metal additive manufacturing uses a continuous wave (CW) laser heat source, some commercial applications of LPBF additive manufacturing instead involve the modulation of the laser power on tens-of-microsecond timescales as an adjustable process variable. This article reports the use of in situ, high speed x-ray and optical imaging to probe melt pool fluid flow, defect formation, and nearby powder motion during LPBF with both modulated and CW laser heat sources. We observe melt pool dynamics unique to modulated laser melting even at very high duty cycles that are related to fluctuations in vapor depression depth, complex pore formation mechanisms, and changes to denudation physics when compared to CW melting. These behaviors are present in Ti–6Al–4V, 316L stainless steel, and AL1100 alloys but vary slightly as a function of material, indicating a substantial dependence on the viscosity and surface tension of the liquid metal. While high duty cycles produce weld tracks of comparable quality to CW melting, lower duty cycles introduce substantial defect concentrations. At intermediate duty cycles, careful control of modulation parameters can repeatably and precisely yield one pore per laser pulse, suggesting a method for intentionally inserting engineered porosity at specific sites during an LPBF build.