Reduction in Brake Wear Emissions with Cr2O3 and WC-CoCr Coatings for Cast Iron Discs

The present contribution showcases the potential brake emission reduction with Cr2O3 (chromium oxide) and WC-CoCr (tungsten carbide–chromium–cobalt) rotor coatings, as realized in our joint public–private research consortium. Particulate matter (PM) emissions from automotive braking systems have been characterized using a pin-on-disc tribometer equipped with particle measurement devices: a CPC (Condensation Particle Counter), an APS (Aerodynamic Particle Sizer), an SMPS (Scanning Mobility Particle Sizer), and a PM2.5 sampling unit. Brake pad samples made from the same low-steel friction material were tested against a grey flake cast iron disc and two types of custom coated discs: a Cr2O3-coated disc and a WC-CoCr-coated disc. The friction pairs were investigated at a constant contact pressure of 1.2 MPa while the sliding velocity varied during the test, starting with 25 sequences at 3.6 m/s, followed by 19 sequences at 6.1 m/s, and finishing with 6 sequences at 11.2 m/s. The test results show encouraging 64% to 84% reductions in particle number (PN) emissions between 4 nm and 3 µm and 84% to 95% reductions in mass emissions (PM2.5) thanks to the respective coated discs. SEM-EDXS (Scanning Electron Microscopy and Energy Dispersive X-ray Spectroscopy) analyses show that the hardness and roughness of the discs, the chemical reactivity (oxidation), and the abrasiveness of the three friction pairs are parameters that might explain this reduction in emission.