Analysis of Strain Hardening Stages of AISI 316 LN Stainless Steel Under Cold Rolling Conditions

In the present investigation, stress–strain curves and strain hardening rates on samples rolled at ambient temperature with thickness reductions of 0%, 10%, 30%, and 50% were studied. On the processed samples, static tensile tests at ambient temperature were performed. Transformation of the engineering stress–strain curves to true stress–strain curves and their numerical processing by first derivation (θ = dσ/dε) was carried out. Dependencies θ = f(εT) characterizing the strain hardening rates were derived. From the curves and the true stress–strain and strain hardening rates, the three stages describing different rates of strain hardening were identified. A rapid increase in true stress and a rapid decrease in the strain hardening rate in Stage I were observed. Quasi-linear dependencies with an increase in true stress but with a slow, gradual decline in the strain hardening rate in Stage II were obtained. Slowly increasing true strains, accompanied by a decrease in strain hardening rates and their transition to softening, led to the formation of plastic instability and necking in Stage III. The endpoints of the strain hardening rate depending on the cold rolling deformations lie in the following intervals: θStage I ∈ <1904;3032> MPa, θStage II ∈ <906;−873> MPa, θStage III ∈ <−144;−11,979> MPa. While in Stage I and Stage II, the plastic deformation mechanism is predominantly dislocation slip, in Stage III, the plastic deformation mechanism is twinning accompanied by dislocation slip.