Investigation on the Mechanical Properties of White Layers by Cutting and Burnishing Coupling Effect in BTA Deep Hole Drilling

The unique cutting–burnishing coupling effect in BTA deep hole drilling generates a high-hardness and -brittleness white layer (ultrafine martensitic layer), which will degrade component performance and accelerate tool wear. This work investigated the formation mechanism and the mechanical properties of the white layer generated in three distinct regions (the cutting edge radius zone, cutting–burnishing corner zone, and guide pad edge zone) through nanoindentation, SEM and BSE. The microstructure and thickness of the white layer under different feedrates are investigated. The correlations between the white layer, the structure of guide pads, and wear behaviors of the TiN- and TiCN/Al2O3-coated guide pads are revealed. Variations in hardness are observed across different zones. The white layer undergoes a soft-to-hard transition due to rapid quenching and the cutting–burnishing effect at the sharp corner. The highest hardness (9.758 GPa) was observed in the guide pad zone, accompanied by grain refinement. The chamfered TiN-coated guide pad exhibits superior wear resistance but suffers fatigue cracking and adhesive wear in the initial guiding zone. The TiCN/Al2O3-coated pad with rounded corners experiences brittle spalling in the mid-to-rear guiding zone. These findings enhance the understanding of the white layer formation in deep hole drilling and provide a foundation for tool optimization.