The Deterioration of Low-Cycle Fatigue Properties and the Fatigue Life Model of Reinforcing Steel Bars Subjected to Corrosion

Thousands of coastal reinforced concrete structures using HRB400 bars have served for over three decades in China. Their reinforcement simultaneously endures chloride corrosion and seismic action, yet studies on performance degradation remain limited. This paper investigates the low-cycle fatigue (LCF) behavior of HRB400 bars under various strain amplitudes, systematically analyzing corrosion morphology, cyclic stress–strain response, fatigue life, and underlying mechanisms. Corrosion is induced by an adjusted accelerated method that replicates field conditions. Observations reveal that corrosion pits act as primary crack initiation sites. Crack paths and fracture surfaces progressively follow the local pit geometry as strain and corrosion grow. The detrimental effect of corrosion on LCF life is more pronounced for smaller bars. At a γ of around 8%, 20 mm bars lose 60.7% of the half cycles to failure at ε = ±1.5%, but only 37.5% at ε = ±5.0%. Predictive corrosion-inclusive strain amplitude (εa)–fatigue life models are proposed, yielding R2 = 0.952 (16 mm) and 0.928 (20 mm). A unified LCF predictive model, calibrated on a database of 310 corroded/uncorroded bar tests, is established. The final model comprehensively considers the characteristics of rebars, seismic action, and corrosion damage, improving the conventional relationship between LCF life and seismic loading. This work contributes to the understanding of the fatigue behavior of HRB400 bars and provides support for time-dependent seismic reliability analysis of aging reinforced concrete structures in corrosive environments.