The Effect of Cr Cathode Arc Current on the Wear Resistance of Cr/(Zr,Cr)N/(Zr,Cr,Al)N Coatings on 7050 Aluminum Alloy

The application of 7050 aluminum alloy in high-friction environments is limited due to its insufficient surface wear resistance. This study aims to enhance its wear resistance by depositing Cr/(Zr,Cr)N/(Zr,Cr,Al)N multilayer composite coatings using filtered cathodic vacuum arc deposition (FCVAD) technology under different Cr cathode arc currents (65A, 85A, 105A, 125A). Coatings were characterized by SEM, EDS, XRD, nanoindentation, and reciprocating wear testing. Results show that increasing arc current from 65 A to 125 A led to grain coarsening, reduced Zr content, and increased Cr-rich microdroplets. Nanoindentation results indicated that the coating prepared under a 65 A current exhibited the best hardness (13.03 GPa) and elastic modulus (242.87 GPa), which is mainly attributed to the formation of fine grains and fewer surface defects under low current conditions. Reciprocating wear tests showed that the wear resistance of all coating samples was superior to that of the uncoated 7050 aluminum alloy substrate. At an arc current of 85 A, the best wear resistance was observed, combining a low wear rate (5.31 × 10−5 mm3) with good mechanical strength (hardness of 8.54 GPa). This study revealed the regulatory mechanism of Cr cathode arc current on the microstructure and performance of Cr/(Zr,Cr)N/(Zr,Cr,Al)N multi-layer composite coatings, providing a theoretical basis and experimental support for optimizing coating process parameters to enhance the wear resistance of aluminum alloy surfaces.