Comprehensive Analysis of Microstructure and Mechanical, Operational, and Technological Properties of AISI 321 Austenitic Stainless Steel at Electron Beam Freeform Fabrication

The aim of this study was to investigate microstructure and the mechanical and operational characteristics of thick and thin walls 3D-built by electron beam additive manufacturing (EBAM). In addition, the milling parameters (rotation speed, feed, and cutting width) were optimized based on simultaneous assessments of Ra roughness on the machined surfaces and material removing rate values. The wall dimensions did not exert a noticeable effect on their chemical compositions, as compared with the original wires used for 3D printing. In comparison, the strength characteristics of the wrought steel (cold-rolled plate) were higher due to finer grains, with both ferrite content and dislocation density being greater as well. In the 3D building process, multiple thermal cycles gave rise to the formation of elongated columnar grains, reducing the strength characteristics. The corrosion rate of the wrought steel was almost twice those of the 3D-printed blanks because of the higher content of both ferrite and twins. By assessing the machinability of the EBAM-built blanks using the stationary milling machine, the cutting forces were comparable due to similar mechanical properties (including microhardness). To improve the removing rate values and reduce the cutting forces, it is recommended to enhance the cutting speeds while not increasing the feeds. For the semi-industrial milling machine, both linear multiple regression and nonlinear neural network models were applied. An integrated approach was proposed that rationally determined both additive manufacturing and post-processing parameters based on a combination of express assessment and analysis of the mechanical, operational, and technological characteristics of built products within a single laboratory complex.