Effect of Chlorhexidine Immersion and Polishing Systems on the Color Stability and Microhardness of BPA-Based and BPA-Free Resin Composite

Objective: This study aimed to evaluate the color stability and microhardness of two resin composites, a BPA-based composite (Luna) and a BPA-free composite (Luna 2), after immersion in chlorhexidine (CHX), using two different polishing protocols. Methods: Disks (7 mm diameter × 2 mm thickness) were prepared and divided into three groups per material: unpolished, Sof-Lex, and FlexiDisc polished (n = 20 per group). The specimens were immersed daily in either 0.12% CHX or distilled water for 21 days. Color change (ΔE) was measured at 7, 14, and 21 days using a spectrophotometer. Microhardness was evaluated at each time point using a Vickers hardness tester (200 g load, 10 s dwell time). Results: Luna 2 exhibited significant discoloration from day 14, while Luna showed significant color change on day 21 (p < 0.05). After 21 days of CHX immersion, unpolished Luna reached a ΔE value of 6.27 ± 1.69, exceeding the clinically acceptable threshold. At 14 days, Sof-Lex polishing significantly improved color stability compared to unpolished controls for both materials (p < 0.05). No significant differences were observed between the two polishing systems over time (p > 0.05). Luna 2 demonstrated significantly higher microhardness at all evaluated time points (p < 0.001). Both composites exhibited slight reductions in microhardness over time, which were more pronounced in Luna (p < 0.001). Conclusions: Polishing enhanced the color stability of both composites. Luna 2 exhibited superior microhardness compared to Luna, and polishing had no significant effect on this property. Given the increasing clinical shift toward BPA-free materials due to biocompatibility concerns, these findings offer relevant guidance for optimizing the long-term esthetic and mechanical performance of modern resin-based restorations.