Investigation of the Melt-Rotation Effects on Fiber Orientation Variation and Geometrical Shrinkage in FRP Injection-Molded Parts

The study focuses on the asymmetric shrinkage typically occurring between the upstream and downstream regions of FRP injection-molded products, a challenge that is particularly difficult to manage and improve. Specifically, two sets of four-cavity systems in one mold were utilized as the experimental platform. One set used a balanced runner (BR) system, and the other used a non-balanced runner (NBR) system. Each cavity in the four-cavity systems contained an ASTM D638 standard specimen with dimensions of 63.5 mm × 9.53 mm × 3.5 mm. Both CAE simulation and experimental methods were applied. The results show that the filling patterns from the simulation analysis closely matched those from the experimental study for both BR and NBR systems. Furthermore, by comparing the geometric shrinkage of the injected parts, significant differences were observed in the dimensional deformation in three directions (<i>x</i>, <i>y</i>, and <i>z</i>) between the NBR and BR systems. Specifically, at the end of the filling region (EFR), there was no noticeable difference in shrinkage along the flow direction, but the shrinkage in the cross-flow and thickness directions was reduced in the NBR system. Additionally, for the same cavity (1C) in both BR and NBR systems, the melt-rotation effect significantly reduced shrinkage in both the cross-flow and thickness directions. These findings strongly suggest that melt rotation can effectively modify the dimensional shrinkage of injection-molded parts. Moreover, fiber orientation analyses of the 1C cavity were also performed using CAE simulation for both BR and NBR systems. The results show that in the NBR system, the melt-rotation effect substantially alters the fiber orientation. Specifically, the fiber orientation tensors in the cross-flow (A₂₂) direction exhibit a decreasing trend. It can be speculated that the melt rotation alters the flow field, which subsequently changes the fiber orientation by reducing the flow-fiber coupling effect, thereby reducing the upstream-to-downstream asymmetry in the cross-flow direction. Through in-depth analysis, it is demonstrated that the correlation between the macroscopic geometric shrinkage and the microscopic fiber orientation changes is highly consistent. Specifically, in the EFR, ΔA₂₂ decreased by 0.0376, improving upstream/downstream shrinkage asymmetry in the cross-flow direction (Ly). Future work will investigate alternative melt-rotation designs and the optimization of model-internal parameters in FOD prediction.