1,10-Phenanthroline-Iron Complex-Derived Fe-N-C Electrocatalysts: Enhanced Oxygen Reduction Activity and Stability Through Synthesis Tuning

The development of electrocatalysts composed of earth-abundant elements is essential for advancing the commercial application of Proton Exchange Membrane Fuel Cells (PEMFC). Among these, single-atom electrocatalysts, such as Fe-N-C, show great promise for the oxygen reduction reaction (ORR). This study aims to improve the ORR activity and stability of Fe-N-C electrocatalysts by fine-tuning the straightforward 1,10-phenanthroline-iron complexation synthesis method. Key parameters, including iron-to-phenanthroline ratio, carbon powder surface area, and pyrolysis temperature were systematically varied to evaluate their influence on the resulting electrocatalysts. The findings of this study revealed that the electrocatalysts synthesized with 1,10-phenanthroline (Phen) and high-surface-area Black Pearls (BP) possessed much better ORR activity than electrocatalysts prepared by using Vulcan carbon (lower surface area). Interestingly, electrocatalysts prepared with BP, but with a non-bidentate nitrogen-containing ligand molecule, such as imidazole, showed a much poorer activity, as the resulting material predominantly consisted of inactive structures, such as encapsulated iron nanoparticles and iron oxide, as evidenced by HR-TEM, EXAFS, and XRD. Therefore, the results suggest that only the synergistic combination of the bidentate ligand phenanthroline (Phen) and the high-surface-area carbon support (BP) favored the formation of ORR-active Fe-N-C single-atom species upon pyrolysis. The study also unveiled a significant enhancement in electrocatalyst stability during accelerated durability tests (and air storage) as the pyrolysis temperature was increased from 700 to 1300 °C, albeit at the expense of ORR activity, likely resulting from the generation of iron particles. Pyrolysis at 1050 °C yielded the electrocatalyst with the most favorable balance of activity and stability in rotating disk measurements, while maintaining moderate durability under PEM fuel cell operation. The insights obtained in this study may guide the development of more active efficient and durable electrocatalysts, synthesized via a simple method using earth-abundant elements, for application in PEMFC cathodes.