Influence of Cooling Methods on Microstructure and Mechanical Properties of TiB2@Ti/AlCoCrFeNi2.1 Eutectic High-Entropy Alloy Matrix Composites

The present study focused on 10 wt.% TiB2@Ti/AlCoCrFeNi2.1 eutectic high-entropy alloy matrix composites (EHEAMCs), which were treated with furnace cooling (FC), air cooling (AC), and water cooling (WC) after being held at 1000 °C for 12 h, aiming to investigate the effect of cooling methods on their microstructure and mechanical properties. The results showed that the composites in all states consisted of FCC phase, BCC phase, TiB2 phase, and Ti phase. The cooling methods did not change the phase types but affected the diffraction peak characteristics. With the increase in cooling rate, the diffraction peaks of FCC and BCC phases gradually separated from overlapping, and the diffraction peak of the FCC (111) crystal plane shifted to a lower angle (due to the increase in lattice constant caused by Ti element diffusion), while the diffraction peak intensity showed a downward trend. In terms of microstructure, all composites under the three cooling conditions were composed of eutectic matrix, solid solution zone, and grain boundary zone. The cooling rate had little effect on the morphology but significantly affected the element distribution. During slow cooling (FC, AC), Ti and B diffused sufficiently from the grain boundary to the matrix, resulting in higher concentrations of Ti and B in the matrix (Ti in FCC phase: 7.4 at.%, B in BCC phase: 8.1 at.% in FC state). During rapid cooling (WC), diffusion was inhibited, leading to lower concentrations in the matrix (Ti in FCC phase: 4.6 at.%, B in BCC phase: 4.3 at.%), but the element distribution was more uniform. Mechanical properties decreased with the increase in cooling rate: the FC state showed the optimal average hardness (627.0 ± 26.1 HV), yield strength (1574 MPa), fracture strength (2824 MPa), and fracture strain (24.2%); the WC state had the lowest performance (hardness: 543.2 ± 35.4 HV and yield strength: 1401 MPa) but was still better than the as-sintered state. Solid solution strengthening was the main mechanism, and slow cooling promoted element diffusion to enhance lattice distortion, achieving the synergistic improvement of strength and plasticity.