A finite-strain rate- and pressure-dependent constitutive framework for analyzing shock compression behavior of cemented tungsten carbides to 100 GPa

In the present study a thermodynamically-consistent finite-strain rate-and-pressure-dependent constitutive framework is implemented to analyze the shock-compression behavior of cemented tungsten carbides to 100 GPa. Central to this framework is the use of logarithmic strain with a set of invariant basis that allow the Cauchy stress tensor to be expressed as a sum of three response terms that are mutually orthogonal, thus permitting a complete separation of the deviatoric and volumetric (pressure) response. An overstress viscoplasticity model that includes strain and strain rate hardening along with thermal softening is used to represent the deviatoric response, while a complete Mie-Grüneisen equation of state (EoS) is used to obtain the pressure response. Using this formulation, the shock-induced compression behavior of cemented tungsten carbide - obtained from planar plate impact experiments using a 30 mm powder gun to peak stresses of up to ∼ 100 GPa - is analyzed to better understand the structure of the measured shock wave profiles and the associated in-material shock quantities. Of particular interest is the evolution of material inelasticity and strength, and temperature in the tungsten carbide samples during the shock compression process. • A Rate-and-pressure-dependent constitutive framework is developed to analyze shock-behavior of WC. • Central to this framework is the use of logarithmic strain with a set of invariant basis. • An overstress viscoplasticity model is employed to represent the deviatoric response. • A complete Mie-Grüneisen equation of state is used to describe the volumetric response. • The formulation is validated using results of plate impact experiments on WC to ∼ 100 GPa.