Boosting Photoelectrochemical Water Splitting via InPOx-Coated TiO2 Nanowire Photoanodes

A hierarchical photoanode composed of amorphous indium phosphate (InPO_x)-coated titanium dioxide nanowires (TiO₂ NWs) was successfully fabricated via a hydrothermal method followed by dip-coating and thermal phosphidation. Structural characterization revealed the formation of a uniform InPO_x shell on the surface of vertically aligned TiO₂ NWs, without altering their 1D morphology. X-ray photoelectron spectroscopy confirmed the incorporation of phosphate species and the presence of oxygen vacancies, which contribute to enhanced interfacial charge dynamics. Photoelectrochemical (PEC) measurements demonstrated that the InPO_x/TiO₂ NWs significantly improved photocurrent density, with the 0.1 M InCl₃-derived sample achieving 0.36 mA·cm^-2 at 1.0 V-an enhancement of approximately 928% over pristine TiO₂. This enhancement is attributed to improved charge separation and injection efficiency (91%), as well as reduced interfacial resistance verified by electrochemical impedance spectroscopy. Moreover, the Mott-Schottky analysis indicated a four-order increase in carrier density due to the InPO_x shell. The modified electrode also exhibited superior stability under continuous illumination for 3 h. These findings highlight the potential of amorphous InPO_x as an effective cocatalyst for constructing efficient and durable TiO₂-based photoanodes for solar-driven water-splitting applications.