Nucleation rate controlled grain boundary and lattice creep

Nucleation versus diffusion rate-limited bicrystal and single crystal creep exhibit different scaling dependencies that enable the mechanisms to be isolated when measured as a function of sample size. It has recently been suggested that nucleation rate-limited kinetic models generally describe the non-Newtonian portion of the creep response well, but more direct evidence is required. This work analyzes the grain boundary creep response of UO 2 , a pyrochlore high entropy oxide, silver, and palladium, along with the lattice creep of silver using small-scale in situ loading in the transmission electron microscope. At small sizes, each system exhibits scale dependence associated with nucleation rate-limited kinetics. Fits of the data produce activation volumes on the order of a few Burgers vectors cubed with positive temperature coefficients as expected for nucleation kinetics. The activation enthalpies fall in the range of about 0.4 eV to 1.7 eV, being lower for the metals and higher for the oxides.