Low-Emission Cement Mortars with Superplasticizer: Temperature-Dependent Performance

The environmental impact of cement production is strongly associated with the high clinker content and its corresponding CO2 emissions. This study examines the performance of low-emission cement mortars incorporating supplementary cementitious materials (SCMs), such as ground granulated blast-furnace slag (GGBFS) and fly ash, which partially replace clinker and contribute to CO2 reduction. Six cement types (CEM I, CEM II/B-V, CEM II/B-S, CEM III/A, CEM V/A (S-V), and CEM V/B (S-V)) were assessed in 104 mortar formulations using a polycarboxylate-based superplasticizer, under varied curing temperatures (10 °C, 20 °C, 29 °C, and 33 °C). The present study is an experimental analysis of the impact of different plasticising and superplasticising admixtures on the demand for admixtures to achieve high flowability and low air content in cement-standardised mortar for admixture testing. PN-EN 480-1. The results indicate that mortars containing CEM III/A and CEM V/B (S-V) exhibited compressive strengths comparable to or superior to CEM I at 28 days, with strength gains exceeding 60 MPa at 20 °C. Workability retention at elevated temperatures was most effective in slag-rich cements. The plasticizing efficiency of the admixture decreased at temperatures above 29 °C, especially in fly ash-rich systems. The incorporation of SCMs resulted in an estimated reduction of up to 60% in clinker, with a corresponding potential decrease in CO2 emissions of 35–45%. These findings demonstrate the technical feasibility of using low-clinker, superplasticized mortars in varying thermal environments, supporting the advancement of sustainable cementitious systems.