Evaluation of Corrosion Behavior of Zn–Al–Mg-Coated Steel in Corrosive Heterogeneous Soil

The long-term durability of steel structures in contact with soil remains a critical challenge due to the complex and aggressive nature of many soil environments. This study presents a thorough evaluation of the corrosion resistance and microstructural evolution of Magnelis® ZM430-coated steel exposed to highly aggressive, heterogeneous soils. Gravimetric analysis revealed that the Magnelis® ZM430 coating exhibits low corrosion rates and enhanced initial barrier properties, even under severe soil conditions. Although the literature frequently reports that Zn–Al–Mg coatings outperform conventional hot-dip galvanized coatings, our results highlight that this superiority is not universal and may be limited under highly aggressive, heterogeneous soils. Microstructural characterization by optical microscopy, SEM/EDS, and XRD demonstrated that the as-received coating consists of a homogeneous layer with well-distributed Zn-, MgZn2-, and Al-rich phases. Upon soil exposure, corrosion preferentially initiates in the Mg- and Al-rich interdendritic and eutectic regions, leading to selective phase depletion and localized breakdown of the protective layer. Despite these localized vulnerabilities, the overall performance of Magnelis® ZM430 remains superior, especially during the early stages of exposure. While no direct comparisons were performed in this work, our findings align with previous literature reporting superior performance of Zn–Al–Mg coatings compared to conventional hot-dip galvanized coatings in similar environments. Importantly, the integration of precise corrosion rate data with detailed soil characterization enables accurate prediction of coating service life, allowing for optimized coating thickness selection and proactive maintenance planning. These findings underscore the value of combining advanced Zn–Al–Mg coatings with site-specific environmental assessment to ensure the long-term integrity of buried steel infrastructure.