Femtosecond Laser Single-Spot Welding of Sapphire/Invar Alloy

Ultrafast laser welding of glass/metal heterostructures has found extensive applications in sensors, medical devices, and optical systems. However, achieving high-stability, high-quality welds under non-optical contact conditions remains challenging due to severe internal damage within glass materials. This study addresses thermal management through synergistic control of thermal accumulation effects and material ablation thresholds. Using the sapphire/Invar alloy system as a model for glass/metal welding, we investigated thermal accumulation effects during ultrafast laser ablation of Invar alloy through theoretical simulations. Under a repetition rate of 1 MHz, the femtosecond laser raised the lattice equilibrium temperature by 700 K within 10 microseconds, demonstrating that high repetition rate femtosecond lasers can induce effective heat accumulation in Invar alloy. Furthermore, ablation thresholds for both materials were determined across varying repetition rates via the D² method, with corresponding threshold curves systematically constructed. Finally, based on the simulation and ablation threshold calculation results, laser parameters were selected for ultrafast laser single point welding of sapphire and Invar alloy. The experimental results demonstrate effective thermal effect mitigation, achieving a maximum shear strength of 63.37 MPa. Comparative analysis against traditional scan welding further validates the superiority of our approach in thermal management. This work provides foundational theoretical and methodological guidance for ultrafast laser welding of glass/metal heterostructures.