Analysis of the Possibility of Increasing the Load-Bearing Capacity and Fatigue Life of CFRP Material Mechanical Joints

Achieving a high load-bearing capacity and fatigue life of joints of composite structures is possible with the use of mechanical fasteners. The aim of this research was to search for effective methods of increasing the load-bearing capacity of mechanical joints of CFRP components. A CFRP composite was made from carbon fabric (KORDCARBON, Czech Republic) using vacuum bag technology. Riveted and bolted joints were evaluated. The pressures exerted on the composite parts during assembly were measured. The values of pressures that cause permanent deformation of the tested composite were estimated. It was shown that the onset of failure of riveted joints is related to the pressures of the shanks of these fasteners on the holes. The load capacity of bolted joints also depends on the pressures of bolt heads on the composite elements. The value of bearing stresses in the pivot-loaded composite was determined. A tomographic study was conducted to determine the damage caused by their interaction. It was shown that the application of a rare-earth adhesive between the threaded bolt shank and the hole results in an increase in the load-bearing capacity of bolted joints by about 10%. A similar increase in strength is observed when the bolt assembly torque is increased.