Investigation of Electrical Conduction Mechanisms in Silicone Rubber—Bismuth Ferrite Composites

Three composite materials, made by inserting the same amount of BiFeO3/Bi25FeO40 powders (each powder having a different concentration of the secondary phase, Bi25FeO40: 10%, 20%, and 30%) into a silicone rubber (SR) matrix, were investigated to understand their electrical properties. Electrical conductivity measurements of the composite samples were carried out over a frequency range from 0.5 kHz to 2 MHz. The resulting conductivity spectra revealed two distinct regions: a low-frequency plateau corresponding to DC conductivity and a high-frequency region where AC conductivity increases with frequency. Some key electrical parameters, such as DC conductivity and band gap energy, were calculated using these measurements. An increase in Bi25FeO40 concentration resulted in a rise in DC conductivity from 5.61 × 10−5 S/m to 7.67 × 10−5 S/m across the composite samples. To gain further insight into the mechanisms of charge transport, both Jonscher’s universal response and the correlated barrier hopping (CBH) model were applied. The polaron model was also used to calculate the energy barrier for electrical conduction, but for higher temperatures (where the samples exhibit conductor behavior). The last part of the study was an aging analysis that showed a degradation of the investigated sample, as reflected by a decline in their conductive properties over time. Having no endothermic or exothermic events in the DTA curves, it is clear that the observed variation in conductive properties is not related to phase transitions, but it can be attributed to microstructural mechanisms, such as defects, microcracks, or structural disorders. These results can help in designing composite materials with desirable conductive properties by optimizing their filler concentration and processing conditions.