Impact of Multiple-Laser Processing on the Low-Cycle Fatigue Behaviour of Laser-Powder Bed Fused AlSi10Mg Alloy

Multi-laser processing is increasingly adopted in laser powder bed fusion (L-PBF) to improve productivity and enable the fabrication of larger components, but its impact on part quality and performance remains a critical concern. This study investigates the microstructure, tensile properties, and fatigue performance of components fabricated by L-PBF using single- and multiple-laser configurations. Both strategies were evaluated under varying layer thicknesses and gas flow conditions with optimized process parameters. Microstructural analysis revealed defects such as lack-of-fusion, porosity and microcracks in multiple-laser builds with reduced gas flow. However, the density and microhardness results showed negligible differences between single and multiple-laser builds. Tensile testing indicated that single-laser builds exhibited superior strength and ductility, whereas multiple-laser builds demonstrated reduced performance due to localized defects such as lack-of-fusion and microcracks. Low-cycle fatigue testing results showed that optimized multiple-laser strategies could achieve performance comparable to that of single-laser builds while improving productivity. The results also revealed that the gas flow becomes more pronounced with multiple-laser processing, where more spatter is generated due to the interactions of the lasers in a small scan area, and that reduced gas flow leads to fatigue degradation due to increased defect density. The results from this study clearly highlight the importance of gas flow, laser overlap, border optimization, and defect mitigation strategies in producing multiple-laser produced components with mechanical properties and fatigue performance comparable to those of single-laser produced L-PBF components.