A reversible solvent segregation transition at grain boundaries in gold-platinum alloys

Solute segregation to grain boundaries in polycrystalline metals and ceramics is a well-known phenomenon that reduces the total energy of the material. In this letter, the segregation of the solvent (Au) to grain boundaries in a binary Au 1-x Pt x ( x = 0.15 to 0.18) alloy is demonstrated. After heating in the range of 500 °C to 600 °C and quenching to room temperature, grain boundaries in the alloy are enriched in Au at a mean level of ∼ 4 atoms/nm 2 . When the alloy is annealed at 300 °C and quenched, the mean grain boundary composition is closer to the bulk composition. When the alloy is reheated to 500 °C, the segregation is reestablished, demonstrating that the transformation from the strongly segregated complexion to the weakly segregated complexion is reversible. The driving force for the solvent segregation is likely the lower grain boundary energy of Au in comparison to Pt.