Experimental Evaluation of Thermal and Moisture Behavior of Stearic Acid-Coated Expanded Perlite for Sustainable Insulation Mortars

In this study, the water-repellent performance of Expanded Perlite (EP) coated with stearic acid (SA) at different coating/EP ratios (0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 1%, 2%, 3%, 4% and 5%) and the capillary water absorption and thermal conductivity behaviors of the modified insulation mortars prepared at these different coating/EP ratios were investigated experimentally. In contrast to the existing literature, experimental studies were carried out for both coated and uncoated EP particles used in mortars to which water-repellent polymers were not added, and the minimum and maximum coating amounts showing the lowest capillary water absorption and slump were determined. In addition, the sustainability of modified insulation mortars consisting of EP-coated SA was determined by sustainable thermal performance (STP). In other words, this study is the first in the literature to determine how the thermal conductivity values of these mortars may change during their use in buildings. According to the experimental results, water absorption, which is an undesirable property, decreased significantly when coated with SA, and even SA-coated expanded coarse perlite (SCP) showed almost no water-absorption behavior at coating levels above 2%. The water-repellent performance of SCP was determined to be 83.2% between 0.1% and 0.4%. In addition, for coarse mortars (MCs), the best water-repellent performance was achieved at a 5% coating/EP ratio, with a 37% reduction in the capillary water-absorption coefficient. In addition, it was found that STP values increased as the coating/EP ratio increased. In other words, modified insulation mortars became more sustainable with an increasing SA coating/EP ratio. The highest STP values were observed in Groups 2 and 4 at a 5% coating/EP ratio, with MC-5 reaching 39.27% in Group 2 and MF-5 reaching 30.30% in Group 4. The results are important from a practical/industrial point of view and from a scientific point of view.