The Influence of the Size of the Brazing Gap on the Structure and Strength of Kovar Joints with Stainless Steel

Comprehensive studies of the influence of brazing gap widths (100, 50, 20 m) on the structure and mechanical properties of brazed dissimilar joints between Kovar and stainless steel, utilizing Cu-Mn-4.5Co-2.5Fefiller metal during high-temperature vacuum brazing, are presented.X-ray microspectral analysis reveals a two-phase structure in the brazed seams, when Cu-Mn-Co-2.5Fe filler metal is employed.This structure consists of both the -Cu phase forming the main zone of the brazed seam (with a 100 or 500 m gap) and discrete grains of the -phase (FeMnyCoz)Me.During brazing, mutual-diffusion processes occur at the interphase boundary between the liquid filler metal and the solid base metal.The filler metal becomes saturated with constituent components of the base metalchromium, cobalt, and nick-elthus, influencing the chemical composition and mechanical properties of the brazed seam.Micro-x-ray spectral analysis indicates that reducing the gap from 100 to 20 m increases the -phase (FeMnyCoz)Me content in the seam from 13.20% to 90.90%, while simultaneously decreasing the -Cu phase from 86.83% to 9.10%.These structural changes positively affect the mechanical properties of the brazed dissimilar joints, leading to increased shear strength in Kovar-stainless steel overlap joints.With a gap size of 20 m, the brazed samples exhibited failure primarily on the stainless steel (600 MPa).