Impact of Hydrofluoric Acid, Ytterbium Fiber Lasers, and Hydroxyapatite Nanoparticles on Surface Roughness and Bonding Strength of Resin Cement with Different Viscosities to Lithium Disilicate Glass Ceramic: SEM and EDX Analysis

This study looks at the effect of surface conditioners hydrofluoric acid (HFA), Ytterbium fibre laser (YFL), and Hydroxyapatite nanoparticles (HANPs) on the surface roughness (Ra) and shear bond strength (SBS) of different viscosity resin cements to lithium disilicate glass ceramic (LDC). A total of 78 IPS Emax discs were prepared and categorized into groups based on conditioning methods. Group 1 HFA–Silane (S), Group 2: YFL-S, and Group 3: HANPs-S. A scanning electron microscope (n = 1) and profilometer (n = 5) were used on each conditioned group for the assessment of surface topography and Ra. A total of 20 LDC discs for each conditioned group were subsequently categorized into two subgroups based on the application of high- and low-viscosity dual-cured resin cement. SBS and failure mode were assessed. ANOVA and post hoc Tukey tests were employed to identify significant differences in Ra and SBS among different groups. LDC conditioned with HFA-S, HANPs-S, and YFL-S demonstrated comparable Ra scores (p > 0.05). Also, irrespective of the type of conditioning regime, the use of low-viscosity cement improves bond values when bonded to the LDC. LDC treated with YFL-S and HANPs-S can serve as an effective substitute for HFA-S in enhancing the Ra and surface characteristics of LDC. The low-viscosity resin cement demonstrated superior performance by achieving greater bond strength.