A Flake Powder Metallurgy Approach for Fabricating Al/CNT Composites: Combining Dual-Matrix and Shift-Speed Ball Milling to Optimize Mechanical Properties

This study presents a novel flake powder metallurgy approach for fabricating Al/CNT composites, combining the dual-matrix (DM) method with shift-speed ball milling (SSBM) to optimize mechanical performance. Samples prepared via DM-SSBM were systematically compared to those produced by conventional high-speed ball milling (HSBM), single-stage SSBM, and dual-matrix (DM) routes. Tensile testing revealed that the DM1MR50-SSBM composite achieved a superior balance of strength and ductility, with an ultimate tensile strength of ~267 MPa, elongation of ~9.9%, and the highest energy absorption capacity (~23.4 MJ/m3) among all tested samples. In contrast, the HSBM sample, while achieving the highest tensile strength (~328 MPa), exhibited limited elongation (~4.7%), resulting in lower overall toughness. The enhanced mechanical response of the DM-SSBM composites is attributed to improved CNT dispersion, refined cold-welding interfaces, and pure Al matrix softness, which together facilitate superior load transfer and hinder crack propagation under tensile stress. In the final consolidated state, aluminum forms a continuous matrix embedding the CNTs, justifying the use of the term “aluminum matrix” to describe the composite structure. These findings highlight the DM-SSBM approach as a promising method for developing lightweight, high-toughness aluminum composites suitable for energy-absorbing structural applications.