Study of New Glass–Ceramic and Dense Ceramic Containing Biogenic Hydroxyapatite

A novel bioactive glass-ceramic was developed using biogenic hydroxyapatite (BHA) synthesized from <i>Rapana venosa</i> (Black Sea) shells and monocalcium phosphate monohydrate [Ca(H₂PO₄)₂·H₂O] via solid-state synthesis. The prepared batches were obtained by combining BHA with SiO₂, B₂O₃, and Na₂O, melted at 1200 °C and melt-quenched in water to form glass-ceramic materials. Dense biogenic hydroxyapatite-based ceramics were successfully sintered at 1200 °C (2 h hold) using a 25 mass % sintering additive composed of 35 mass % B₂O₃, 45 mass % SiO₂, 10 mass % Al₂O₃, and 10 mass % Na₂O. Structural characterization was carried out using X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The resulting materials consisted of a well-defined crystalline hydroxyapatite phase [Ca₁₀(PO₄)₆(OH)₂] alongside an amorphous phase. In samples with increased SiO₂ and reduced B₂O₃ content (composition 3), a finely dispersed Na₃Ca₆(PO₄)₅ crystalline phase appeared, with a reduced presence of hydroxyapatite. Bioactivity was assessed in simulated body fluid (SBF) after 10 and 20 days of immersion, confirming the material's ability to support apatite layer formation. The main structural units SiO₄, PO₄, and BO₃ are interconnected through Si-O-Si, B-O-B, P-O-P, and mixed Si-O-Al linkages, contributing to both structural stability and bioactivity.