Stoichiometry of Bulk Nb1−βSnβ Superconductors Synthesised by Arc Melting

We present an alternative process for production of binary Nb_1-βSn_β superconducting phases using pre- and post-treatment of arc-melted Nb + Sn ingots. This process combines sequential sintering, arc melting, and annealing procedures that provide dense, bulk samples of Nb_1-βSn_β with varying stoichiometry between 0.18 < β < 0.25 depending on annealing time and temperature. We show, through magnetization measurements of these Nb_1-βSn_β bulks, that annealing of arc-melted samples at 900 °C for 3 h significantly enhances <i>J</i>_c values compared with arc-melted Nb_1-βSn_β samples without annealing. Microstructural analyses show that optimum grain size and orientation are achieved by sintering and annealing at lower temperatures (i.e., 720 °C and 900 °C, respectively) with short annealing times (i.e., <10 h). Processing at higher temperatures and for longer times enhances grain growth and results in fewer pinning centres. The optimum process creates effective pinning centres that deliver a <i>J</i>_c = 6.16 × 10⁴ A/cm² at 10 K (and ~0.2 T), compared with <i>J</i>_c = 3.4 × 10⁴ A/cm² for Nb_1-βSn_β subjected to a longer annealing time at a higher temperature and <i>J</i>_c = 775 A/cm² for an arc-melted sample without post-annealing. We suggest that further work addressing post-treatment annealing times between 3 h < t_post < 60 h at temperatures between 900 °C and 1000 °C will provide the opportunity to control stoichiometric and microstructural imperfections in bulk Nb_1-βSn_β materials.