Effect of Y₂O₃ and B₂O₃ co-doping on the properties of Cr-free zinc oxide varistors

Metal Oxide Arrestor ( MOA ) provides reliable insulation protection for power transmission and transformation equipment with its excellent performance, and is widely used in power generation, transmission, transformation and distribution. As the core component of MOA, the performance of ZnO varistor determines the level of protection. The Y<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf>O<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> and B<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf>O<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> co-doped ZnO varistors were studied. Several tests were carried out on the samples, including phase composition, microstructure, density and electrical properties. The results show that the doping of Y<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf>O<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> and B<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf>O<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> optimizes the spinel phase distribution and increases the number of effective grain boundaries. In addition, Y<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf>O<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> and B<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf>O<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> react with other additives to form a glass phase in the reaction, which has good meshing performance with the grains and increases the densification level. When 1.0 mol % Y<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf>O<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> and 0.1 mol % B<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</inf>O<inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</inf> are added, the ZnO varistor has the best performance: the voltage gradient is 626 V / mm, the leakage current is 0.09 μA, and the nonlinear coefficient is 60. The formula used in this paper does not add Cr element, which is in line with the concept of green manufacturing. On the basis of environmental protection, the excellent performance of ZnO varistor is maintained, which provides a new idea for the research and development of environmentally friendly zinc oxide varistor.