Enhanced Hydrothermal Stability and Propylene Selectivity of Electron Beam Irradiation-Induced Hierarchical Fluid Catalytic Cracking Additives

A cheap, environmentally friendly, easily scalable post-treatment of Na-ZSM-5 (Si/Al molar ratio = 20 or 30) via electron-beam irradiation to produce hierarchical H-ZSM-5 as a propylene-increasing fluid catalytic cracking additive was performed. Higher specific surface areas and highly accessible porous systems were obtained among the irradiated samples. A combination of 27Al, 1H magic angle spinning nuclear magnetic resonance and NH3-temperature-programmed desorption methods showed that upon irradiation, some of the framework’s tetrahedral Al atoms were removed as non-framework Al atoms via flexible coordination with Si-OH groups (either framework or non-framework defects), thus increasing the H-ZSM-5 acidity and stability during hydrothermal dealumination. The enhanced selectivity and stability toward propylene production over the irradiated H-ZSM-5 samples were attributed to the integration of the reserved population of medium acid sites into the highly accessible hierarchical network. N2 adsorption–desorption isotherm data showed that the Si-rich H-ZSM-5 samples possessed an obvious ink-bottle-shaped micro-mesopore network and a greater degree of disordered orientation of the straight pore systems toward the exterior surfaces. Micro-activity test data suggested that with an increasing Si/Al ratio, the H-ZSM-5 additives lost some extent of their cracking activity due to the constricted hierarchical pore network toward the exterior surface but gained more stability and selectivity for propylene due to the reserved medium acid sites.